Analisis Pengendalian Kualitas pada Proses Pembuatan Wingnut Dengan Metode Kaizen Studi Kasus PT Putra Sulung Makmur Metal Castindo

Homan, Kenttaro and Al-Faritsy, Ari Zaqi (2023) Analisis Pengendalian Kualitas pada Proses Pembuatan Wingnut Dengan Metode Kaizen Studi Kasus PT Putra Sulung Makmur Metal Castindo. ["eprint_fieldopt_thesis_type_tugasakhir" not defined] thesis, University of Technology Yogyakarta.

[img] Text
5190611196 KENTTARO HOMAN-ABSTRAK.pdf

Download (117kB)

Abstract

Abstrak PT Putra Sulung Makmur Metal Castindo adalah perusahaan yang telah lama bergerak dalam bidang industri pengecoran logam. Dalam proses produksinya PT Putra Sulung Makmur Metal Castindo sering kali mengalami kendala, terjadinya defect yang tinggi pada hasil produksi wingnut. Ada empat jenis defect yang terjadi pada hasil produksi wingnut pada bulan November 2022 yaitu Gas Hole sebanyak 1514 pcs, Crack sebanyak 1722 pcs, Pin Hole sebanyak 1438 pcs dan Sandinclusion sebanyak 1914 pcs dengan total keseluruhan defect sebanyak 6588 pcs. Dimana keadaan tersebut menyebabkan masalah bagi perusahaan. Tujuan penelitian ini adalah untuk untuk menganalisis faktor-faktor yang menyebabkan cacat produk, untuk mengetahui apakah tingkat defect yang dihasilkan berada dalam batas kendali, dan untuk memberikan usulan rencana perbaikan agar dapat meminimalisir tingkat defect yang dihasilkan pada setiap proses produksi. Penelitian ini menggunakan metode penerapan enam langkah Kaizen beserta tools Kaizen (why-why analysis, 5W1H, dan 5S) dan seven tools yaitu langkah pertama menentukan tema, langkah kedua memahami situasi dan menentukan target, langkah ketiga melakukan identifikasi akar masalah, langkah keempat menentukan recanan perbaikan, langkah kelima melaksanakan perbaikan, dan langkah keenam adalah membandingkan hasil sebelum dan sesudah penerapan usulan perbaikan. Hasil penelitian ini menunjukkan bahwa dengan diterapkannya enam langkah Kaizen dapat meminimalisir tingkat defect yang dihasilkan, yang dimana sebelum perbaikan tingkat kemampuan departeman produksi untuk menghasilkan produk wingnut yang baik pada saat sebelum implementasi perbaikan yakni 89 %. Setelah dilakukannya tindakan perbaikan, kapabilitas proses untuk departemen produksi naik menjadi sebesar 95% dengan kata lain kapabilitas proses naik sebesar 6%. Kata kunci: Kaizen, Seven tools, why-why analysis, 5S, 5W+1H Analysis of Quality Control in the Wingnut Manufacturing Process with the Kaizen Method Case Study of PT Putra Sulung Makmur Metal Castindo ABSTRACT PT Putra Sulung Makmur Metal Castindo is a company that has been engaged in the metal casting industry for a long time. In the production process, PT Putra Sulung Makmur Metal Castindo often experiences problems, such as high defects in wingnut production. Four defects occurred in wingnut production in November 2022, 1514 pcs of Gas Holes, 1722 pcs of Cracks, 1438 pcs of Pin Holes, and 1914 of Sandinclusion pcs with a total defect of 6588 pcs. Where these circumstances cause problems for the company, this study aims to analyze the factors that cause product defects, determine whether the resulting defect rate is within the control limits, and propose improvement plans to minimize the resulting defect rate in each production process. This study uses the six-step Kaizen implementation method, the Kaizen tools (why-why analysis, 5W1H, and 5S), and the seven tools. Namely, the first step determines the theme, and the second step understands the situation and the target, the third step identifies the root of the problem, and the fourth step determines the plan. Improvement, the fifth step is carrying out the improvement, and the sixth step compare the results before and after implementing the proposed improvement. This study's results indicate that implementing the six Kaizen steps can minimize the defect rate of 89% before the repair. After the corrective actions were taken, the process capability of the production department increased to 95%. In other words, the process capability increased by 6%. Keywords: Kaizen, Seven tools, why-why analysis, 5S, 5W+1H

Item Type: Thesis (["eprint_fieldopt_thesis_type_tugasakhir" not defined])
Subjects: T Technology > TS Manufactures
Divisions: Fakultas Sains dan Teknologi > S1 Teknik Industri
Depositing User: Kaprodi S1 Teknik Industri UTY
Date Deposited: 26 May 2023 04:43
Last Modified: 26 May 2023 04:43
URI: http://eprints.uty.ac.id/id/eprint/13091

Actions (login required)

View Item View Item