PEMANFATAN FLY ASH SEBAGAI VARIASI SUBSTITUSI SEMEN DAN VARIASI SERBUK BESI SEBAGAI SUBSTITUSI AGREGAT HALUS PEMBUATAN PAVING BLOCK UTILIZATION OF FLY ASH AS A VARIATION OF CEMENT SUBSTITUTION AND IRON POWDER RADIATION AS A SUBSTITUTION OF FINE AGGREGATE FOR PAVING BLOCK PRODUCTION

Fratama, Andy and Masagala, Algazt Aryad (2023) PEMANFATAN FLY ASH SEBAGAI VARIASI SUBSTITUSI SEMEN DAN VARIASI SERBUK BESI SEBAGAI SUBSTITUSI AGREGAT HALUS PEMBUATAN PAVING BLOCK UTILIZATION OF FLY ASH AS A VARIATION OF CEMENT SUBSTITUTION AND IRON POWDER RADIATION AS A SUBSTITUTION OF FINE AGGREGATE FOR PAVING BLOCK PRODUCTION. Tugas Akhir thesis, University Of Technology Yogyakarta.

Text 5190811010_ANDY FRATAMA_ABSTRAK - Andi Fratama.pdf Download (70kB)

Abstract

Paving Block merupakan bahan bangunan yang terbuat dari campuran semen portland, air dan agregat dengan atau tanpa bahan tambah lainnya yang tidak mengurangi mutu beton tersebut. Dengan komposisi tertentu paving block mempunyai permukaan semi permeable atau permeable yang dapat meneruskan air kedalam tanah. Paving block dimanfaatkan sebagai lapis perkerasan baik di dalam bangunan atau di luar. Penelitian ini berfokus pada penggunaan limbah Fly ash sebagai substitusi semen dengan persentase 10% dan serbuk besi sebagai substitusi agregat halus pada pembuatan paving block. Tujuan dari penelitian ini adalah untuk mengetahui Pengaruh penambahan Fly Ash Sebagai Substitusi Semen Dengan Persentase 10% Dan Serbuk besi 10%, 20%, 30% Sebagai Substitusi Agregat Halus terhadap kuat tekan dan daya serap air paving block, dengan umur rencana pengujian adalah 28 hari. Hasil pengujian menunjukkan bahwa paving block penambahan Fly Ash Sebagai Substitusi Semen Dengan Persentase 10% Dan Serbuk besi 10%, 20%, 30% Sebagai Substitusi Agregat Halus mendapatkan hasil berupa peningkatan dan penurunan nilai kuat tekan paving block sebesar 24,17 MPa, 20.18 MPa, 19,32 MPa, dengan presentase peningkatan sebesar 18,63%, -0,96%, dan -5,19% apabila dibandingkan dengan paving block normal. Sedangkan untuk pengujian daya serap air menunjukkan bahwa paving block penambahan Fly Ash Sebagai Substitusi Semen Dengan Persentase 10% Dan Serbuk besi 10%, 20%, 30% Sebagai Substitusi Agregat Halus secara keseluruhan mendapatkan hasil berupa peningkatan dan penurunan nilai daya serap air paving block sebesar 3,27%, 4,05%, 7,83%, dengan presentase penurunan daya serap air sebesar -47,65%, -35,15%, dan 25,44% apabila dibandingkan dengan paving block normal. Kata Kunci: paving block, Fly ash, Serbuk besi. Paving Block is a building material made from a mixture of portland cement, water and aggregate with or without other additives which do not reduce the quality of the concrete. With a certain composition, paving blocks have a semi-permeable or permeable surface that can transmit water into the ground. Paving blocks are used as a pavement layer both inside and outside the building. This research focuses on the use of fly ash as a substitute for cement with a percentage of 10% and iron filings as a substitute for fine aggregate in the manufacture of paving blocks. The purpose of this study was to determine the effect of adding fly ash as a cement substitution with a percentage of 10% and 10%, 20%, 30% iron filings as a fine aggregate substitution on the compressive strength and water absorption of paving blocks, with a test plan age of 28 days. . The test results showed that the addition of fly ash as a substitute for cement with a percentage of 10% and 10%, 20%, 30% iron powder as a substitute for fine aggregate resulted in an increase and decrease in the compressive strength of paving blocks of 24.17 MPa, 20.18 MPa. , 19.32 MPa, with percentage increases of 18.63%, -0.96% and -5.19% when compared to normal paving blocks. Meanwhile, the water absorption test showed that the addition of fly ash as a substitute for cement with a percentage of 10% and 10%, 20%, 30% iron powder as a substitute for fine aggregate as a whole resulted in an increase and decrease in the water absorption value of paving blocks by 3.27%, 4.05%, 7.83%, with a percentage decrease in water absorption of -47.65%, -35.15% and 25.44% when compared to normal paving blocks. Keywords: paving block, Fly ash, Iron powder.

Item Type:	Thesis (Skripsi, Tugas Akhir or Kerja Praktek) (Tugas Akhir)
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Fakultas Sains dan Teknologi > S1 Teknik Sipil
Depositing User:	Kaprodi S1 Teknik Sipil UTY
Date Deposited:	19 Jun 2026 04:06
Last Modified:	19 Jun 2026 04:06
URI:	http://eprints.uty.ac.id/id/eprint/20094

Actions (login required)

View Item