PENGARUH PENAMBAHAN SERAT POLIMER PET (POLYETHYLENE TEREPHTHALATE) PERSENTASE 0,1%, 0,3%, DAN 0,5% TERHADAP KUAT LENTUR BETON THE EFFECT OF 0.1%, 0.3%, AND 0.5% PERCENTAGE ADDITION OF PET POLYMER FIBER (POLYETHYLENE TEREPHTHALATE) ON THE FLEXIBLE STRENGTH OF CONCRETE

Rahma, Fadhilah Atha and Kurniati, Dwi (2023) PENGARUH PENAMBAHAN SERAT POLIMER PET (POLYETHYLENE TEREPHTHALATE) PERSENTASE 0,1%, 0,3%, DAN 0,5% TERHADAP KUAT LENTUR BETON THE EFFECT OF 0.1%, 0.3%, AND 0.5% PERCENTAGE ADDITION OF PET POLYMER FIBER (POLYETHYLENE TEREPHTHALATE) ON THE FLEXIBLE STRENGTH OF CONCRETE. Tugas Akhir thesis, University Of Technology Yogyakarta.

Text 5190811249_FADHILAH ATHA RAHMA_ABSTRAK - Fadhilah Rahma official.pdf Download (38kB)

Abstract

Balok Beton merupakan beton yang pembuatannya menggunakan bahan baku semen Portland, agregat halus, dan agregat kasar. Semakin berkembangnya dunia kontruksi maka perlu dilakukan peningkatan mutu, dengan cara menambahkan bahan campur. Tugas Akhir ini bertujuan untuk mengetahui nilai kuat lentur dan klasifikasi mutu Beton dengan campuran serat polimer PET sebagai bahan tambah menggunakan subtitusi semen dengan persentase 0,1%, 0,3%, dan 0,5%.Metode yang digunakan dalam penelitian ini yaitu metode experimental. Adapun pengujian ini dengan menggunakan benda uji berjumlah 12 sempel yang teridiri dari 3 sampel beton normal, 3 sampel beton dengan bahan tambah serat plastik polimer PET sebesar 0,1%, 3 sampel beton dengan bahan tambah serat plastik polimer PET sebesar 0,3%, dan 3 sampel beton dengan bahan tambah serat plastik polimer PET sebesar 0,5%.Hasil analisis menunjukkan bahwa nilai kuat lentur balok beton normal sebesar 5,82 MPa, untuk balok beton dengan bahan tambah serat plastik polimer PET 0,1% didapat nilai kuat lentur 5,87 MPa, untuk balok beton dengan bahan tambah serat plastik polimer PET 0,3% didapat nilai kuat lentur 5,78 MPa, dan untuk balok beton dengan bahan tambah serat plastik polimer PET 0,5% didapat nilai kuat lentur 5,69 MPa Kata Kunci : Beton, PET, Kuat Lentur, Mutu Concrete blocks are concrete that is made using Portland cement, fine aggregate and coarse aggregate as raw materials. Due to the growing world of construction, it is necessary to improve quality, by adding mixed materials. This final project aims to determine the value of flexural strength and quality classification of concrete with a mixture of PET polymer fiber as an added material using cement substitution with a percentage of 0.1%, 0.3% and 0.5%. The method used in this study is the experimental method. This test was carried out using 12 specimens consisting of 3 normal concrete samples, 3 concrete samples with 0.1% PET polymer plastic fiber added, 3 concrete samples with 0.3% PET polymer plastic fiber added. , and 3 samples of concrete with the addition of 0.5% PET polymer plastic fiber. The results of the analysis show that the flexural strength value of normal concrete blocks is 5.82 MPa, for concrete blocks with the addition of 0.1% PET polymer plastic fiber, the flexural strength value is 5.87 MPa, for concrete blocks with added PET polymer plastic fiber 0 .3% obtained a flexural strength value of 5.78 MPa, and for concrete blocks with the addition of 0.5% PET polymer plastic fiber obtained a flexural strength value of 5.69 MPa Keywords: Concrete, PET, Flexural Strength, Quality

Item Type:	Thesis (Skripsi, Tugas Akhir or Kerja Praktek) (Tugas Akhir)
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Fakultas Sains dan Teknologi > S1 Teknik Sipil
Depositing User:	Kaprodi S1 Teknik Sipil UTY
Date Deposited:	19 Jun 2026 08:33
Last Modified:	19 Jun 2026 08:33
URI:	http://eprints.uty.ac.id/id/eprint/20175

Actions (login required)

View Item