Azra, Abdurrazak Prananda and Ismaili, Abul Fida (2019) PENGARUH PENAMBAHAN SERAT KAWAT BENDRAT DENGAN KADAR 0,5%, 1,5%, 2,5% PADA BETON DENGAN TEKNOLOGI FOAMING TERHADAP KUAT TEKAN, KUAT LENTUR DAN MODULUS ELASTISITAS. Tugas Akhir thesis, University Technology Yogyakarta.
|
Text
1. Abdurrazak Prananda Azra.docx.pdf Download (188kB) | Preview |
Abstract
ABSTRAK Beton ringan dengan teknologi foaming diperoleh dengan cara meniadakan agregat kasar dan memasukkan rongga udara (stable foam) didalam beton, pembuatan rongga udara didalam beton menggunakan foaming agent. Solusi untuk meningkatkan kuat tekan, kuat lentur dan modulus elastisitas yang dimiliki beton ringan yaitu dengan menambahkan serat kawat bendrat. Persentase serat kawat bendrat yang dilakukan adalah 0,5%, 1,5% dan 2,5%. Metode yang digunakan adalah metode eksperimen yang dilaksanakan di laboratorium Bahan Struktur Fakultas Teknik STTNAS. Untuk pengujian kuat tekan dan modulus elastisitas berbentuk silinder dengan diameter 30 cm dan tinggi 60 cm, pengujian kuat lentur digunakan benda uji berbentuk balok dengan dimensi 15 cm x 15 cm x 60 cm. Penelitian ini dilakukan untuk membandingkan beton ringan normal dengan beton ringan bahan tambah foaming agent dan serat kawat bendrat. Dari hasil analisis yang telah dilakukan untuk kuat tekan rata-rata dengan persentase 0%, 0,5%, 1,5%, 2,5% sebesar 5,3 MPa; 6,2 MPa; 6,8 MPa dan 8,93 MPa, dengan peningkatan 16,98%; 28,3%; dan 68,49% dari kuat tekan beton ringan foaming tanpa serat. Kuat Lentur rata-rata beton ringan foaming berserat kawat bendrat dengan persentase 0%, 0,5%, 1,5%, 2,5% berturut-turut adalah 1,8 MPa; 2,1 MPa; 2,8 MPa dan 4,3 MPa atau terjadi perubahan terbesar adalah sebesar 115,24% dari kuat lentur beton ringan foaming tanpa serat. Modulus elastisitas dengan kadar serat 0%, 0,5%, 1,5%, 2,5% berturut-turut adalah 5007,56 MPa; 5505,79 MPa; 5700,34 MPa; 6129, 53 MPa atau terjadi perubahan maksimum pada kadar serat 2,5% sebesar 22,41% dibandingkan dengan beton ringan foaming tanpa serat. Kata Kunci: Beton, foaming, tekan, lentur, modulus ABSTRACT Lightweight concrete with foaming technology obtained by removing coarse aggregate and putting air cavity (stable foam) into the concrete, making air cavity inside the concrete using foaming agent. Solution to increase compressive strength, flexural strength, and modulus of elasticity in the lightweight concrete is by adding bendrat wire fiber. The percentages of bendrat wire fiber are 0.5%, 1.5%, and 2.5%. The method used is experimental method conducted in the laboratory of structure material of Faculty of Technic of STTNAS. For testing compressive strength and modulus of elasticity in cylindrical shape with diameter of 30 cm and weight of 60 cm, the test of flexural strength used in the tested object in block shape with dimension of 15 cm x 15 cm x 60 cm. This research is conducted to compare normal lightweight concrete with lightweight concrete using additional material of foaming agent and bendrat wire fiber. Based on the analysis that has been conducted, the results of the test for compressive strength with percentage 0%, 0.5%, 1.5%, 2.5% are 5.3 MPa; 6.2 MPa; 6.8 Mpa, and 8.93 Mpa, with the increase of 16.98%, 28.3%, and 68.49% of compressive strength of lightweight foamed concrete without fiber. The average values of flexural strength of lightweight foamed concrete with bendrat wire fiber in the percentage of 0%, 0.5%, 1.5%, 2.5% are 1.8 MPa; 2.1 MPa; 2.8 MPa and 4.3, respectively, or there is a big change as many as 115.24% of the flexural strength of foamed lightweight concrete without fiber. Modulus of elasticity with the levels of fiber of 0%, 0.5%, 1.5%, 2.5% are 5007.56 Mpa, 5505.79 Mpa, 5700.34 Mpa, 6129. 53 Mpa or there is maximum change on the level of fiber of 2.5% as many as 22.41% compared to the lightweight foamed concrete without fiber. Keywords: Concrete, foaming, compression, flexure, modulus
| Item Type: | Thesis (Skripsi, Tugas Akhir or Kerja Praktek) (Tugas Akhir) |
|---|---|
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) |
| Divisions: | Fakultas Sains dan Teknologi > S1 Teknik Sipil |
| Depositing User: | Kaprodi S1 Teknik Sipil UTY |
| Date Deposited: | 09 May 2019 06:58 |
| Last Modified: | 09 May 2019 06:58 |
| URI: | http://eprints.uty.ac.id/id/eprint/2775 |
Actions (login required)
 |
View Item |