Pambudi, Ifnain Setyo and Susilo, Dibyo (2020) ANALISIS PENGARUH PENAMBAHAN POZZOLAN BONGGOL JAGUNG DENGAN PERSENTASE 4%, 6%, DAN 10% TERHADAP KUAT GESER MORTAR PASANGAN BATU BATA DENGAN VARIASI KETEBALAN 1,5 CM ANALYSIS OF THE EFFECT OF ADDING POZZOLAN CORN WITH A PERCENTAGE OF 4%, 6%, AND 10% ON THE SHIFT STRENGTH OF THE MORTAR OF BRICK PAIRS WITH A VARIATION OF 1.5 CM THICKNESS. Tugas Akhir thesis, University Technology Yogyakarta.
|
Text
5140811145_IFNAIN SETYO P.pdf Download (149kB) | Preview |
Abstract
ABSTRAK Perkembangan dunia konstruksi saat ini menuntut penyedia bahan bangunan menyediakan kebutuhan pasar yang semakin meningkat. Karena kebutuhan yang banyak, maka akan menuntut untuk menyediakan bahan alternatif yang bisa memberi opsi lain ketika bahan yang biasa kita gunakan suatu ketika tidak bisa dipakai kembali. Indonesia merupakan Negara agraris dengan hasil pertanian yang luar biasa. Salah satu hasil pokonya adalah tanaman jagung, dengan memanfaatkan limbah sisa dari tanaman jagung yaitu bonggol jagung maka bonggol jagung diolah menjadi bahan campuran pada adukan mortar. Tujuan penelitian mencoba membandingkan nilai kuat geser mortar dengan campuran standar dengan mortar dengan penambahan pozzolan abu bonggol jagung. Metode penelitian yang dilakukan adalah metode eksperimen atau pengujian. Persentase campuran yang digunakan mortar adalah 4%, 6%, dan 10%. Penelitian dilakukan di laboraturium teknik Universitas Negeri Yogyakarta. Pengujian dilakukan masing-masing dilakukan 3x dan diambil nilai rata-rata. Hasil pengujian kuat tekan kubus adalah 8,35 Mpa, kuat geser mortar pada pasangan batu bata standar 0,16 Mpa, pada campuran pozzolan 4% adalah 0,12 Mpa, pada campuran pozzolan 6% adalah 0,03 Mpa, pada campuran pozzolan 10% adalah 0,11 Mpa. Dari hasil pengujian didapatkan kesimpulan nilai hasil pengujian kuat geser dimana mortar dengan campuran pozzolan abu Bonggol jagung kekuatanya menurun dibanding campuran mortar normal. Berdasarkan hasil pengujian maka campuran abu bonggol jagung pada mortar tidak disarankan untuk digunakan. Kata kunci : Bonggol Jagung, Kuat Geser, Pozzolan Abstract Today's construction world demands building material providers to provide an increasing market demand. Due to the large needs, it will be demanding to provide alternative materials that can provide other options when the materials we usually use cannot be reused one day. Indonesia is an agricultural country with extraordinary agricultural products. One of the main products is the corn plant. By utilizing the residual waste from the corn plant, namely corn cobs, the corn cobs are processed into a mixture in the mortar mixture. The purpose of this study was to try to compare the shear strength value of mortar with a standard mixture with mortar with the addition of corncob ash pozzolan. The research method used was an experimental or testing method. The percentages of the mixture used mortar were 4%, 6%, and 10%. The research was conducted in the engineering laboratory, Yogyakarta State University. Each test was performed 3 times and the average value was taken. The result of the cube compressive strength test was 8.35 Mpa, the mortar shear strength in standard masonry was 0.16 Mpa, for the 4% pozzolan mixture it was 0.12 Mpa, for the 6% pozzolan mixture it was 0.03 Mpa, for the 10 pozzolan mixture % was 0.11 Mpa. From the test results, it was concluded that the value of the shear strength test results where the mortar with a mixture of pozzolan ash corncob has decreased strength compared to the normal mortar mixture. Based on the test results, the mixture of corncob ash in the mortar was not recommended to use. Keywords: Corn Cob, Shear Strength, Pozzolan
| Item Type: | Thesis (Skripsi, Tugas Akhir or Kerja Praktek) (Tugas Akhir) |
|---|---|
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) |
| Divisions: | Fakultas Sains dan Teknologi > S1 Teknik Sipil |
| Depositing User: | Kaprodi S1 Teknik Sipil UTY |
| Date Deposited: | 21 Oct 2020 01:56 |
| Last Modified: | 21 Oct 2020 01:56 |
| URI: | http://eprints.uty.ac.id/id/eprint/5935 |
Actions (login required)
 |
View Item |