PENGARUH PEMANFAATAN SERBUK ARANG KAYU ASAM SEBAGAI BAHAN PENGGANTI PASIR TERHADAP KUAT TEKAN BATAKO THE EFFECT OF THE UTILIZATION OF ACID WOOD CHARCOAL POWDER AS A SAND SUBSTITUTE MATERIAL ON THE COMPRESSION STRENGTH OF BRICK

Wiyasa, Krisna Dwipayana and Kurniati, Dwi (2022) PENGARUH PEMANFAATAN SERBUK ARANG KAYU ASAM SEBAGAI BAHAN PENGGANTI PASIR TERHADAP KUAT TEKAN BATAKO THE EFFECT OF THE UTILIZATION OF ACID WOOD CHARCOAL POWDER AS A SAND SUBSTITUTE MATERIAL ON THE COMPRESSION STRENGTH OF BRICK. ["eprint_fieldopt_thesis_type_tugasakhir" not defined] thesis, University Technology Yogyakarta.

Text 5170811156_Krisna Dwipayana Wiyasa_Abstrak - Krisna Dwipayana.pdf Download (537kB)

Abstract

Zaman semakin maju dan berkembang, iptek memberikan pengaruh besar bagi seluruh aspek kehidupan. Salah satunya adalah teknologi konstruksi yang sudah semakin maju. Arang kayu salah satu bahan yang dapat digunakan sebagai pengganti pasir. Pemanfaatan limbah arang kayu sebagai bahan pengganti pasir dalam campuran batako memiliki prospek yang sangat baik di masa depan baik dari sumber dayanya yang masih sangat banyak maupun potensinya terhadap massa batako. Arang kayu asam memiliki kandungan silika oksida (SiO2) sebagai pengikat yang bagus terhadap kapur, sehingga arang kayu dapat menjadi bahan pengganti pasir. Tujuan dilakukannya penelitian ini adalah mengetahui pengaruh arang kayu asam pengganti pasir terhadap kuat tekan batako dan mengetahui perbedaan kuat tekan batako arang kayu asam dengan batako normal. Pembuatan penelitian ini menggunakan metode analisis data. Menggunakan mix design mortar denga arang kayu asam sebagai pengganti agregat halus (pasir) kemudian dicetak menggunakan cetakan batako manual. Untuk memperoleh data dilakukan pengujian material yang dilaksanakan di laboratorium Balai Teknik Sabo dan PT. Aneka Darma Persada. Pengujian kuat tekan batako dilaksanakan di laboratorium Universitas Teknologi Yogyakarta. Dengan SNI 03-0349-1989 sebagai acuan penelitian. Penelitian ini berfokus pada pmanfaatan arang kayu asam sebagai bahan pengganti pasir. Dari hasil pengujian kuat tekan batako dengan menggunakan bahan serbuk arang kayu asam didapatkan kuat tekan rata-rata 18,92 kg/cm2 dan untuk batako normal didapatkan kuat tekan rata-rata 26,54 kg/cm2. Dalam pencetakan batako direkomendasikan menggunakan mesin daripada manual sehingga mendapatkan hasil yang lebih maksimal. Kata kunci: Arang Kayu Asam, Batako, Kuat Tekan. The era is getting more advanced and developing, science and technology have a significant influence on all aspects of life. One of them is the increasingly advanced construction technology. Wood charcoal is one of the materials that can substitute for sand. The utilization of wood charcoal waste as a substitute for sand in the bricks mixture has excellent prospects in the future, both from its abundant resources and its potential for the bricks’ mass. Acid wood charcoal contains silica oxide (SiO2) as an excellent binder to lime so that wood charcoal can be a substitute for sand. This study aimed to determine the effect of tamarind charcoal instead of sand on the compressive strength of bricks and determine the difference between the compressive strength of tamarind charcoal bricks and standard bricks. Doing this research uses the data analysis method. Using a mixed design mortar with tamarind charcoal as a fine aggregate (sand) substitute, then molded using a manual brickmould. To obtain data, material testing was carried out in the laboratory of the Sabo Engineering Center and PT Various Dharma Persada. The compressive strength test of the bricks was carried out in the laboratory of the Yogyakarta Technological University. With SNI 03-0349-1989 as a research reference. This research focuses on using tamarind charcoal as a substitute for sand. From the results of testing the compressive strength of bricks using tamarind wood charcoal powder, the average compressive strength was 18.92 kg/cm2, and for standard bricks, the average compressive strength was 26.54 kg/cm2. In brick printing, it is recommended to use a machine rather than manually to get maximum results. Keywords: Acid Wood Charcoal, Brick, Compressive Strength

Item Type:	Thesis (["eprint_fieldopt_thesis_type_tugasakhir" not defined])
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Fakultas Sains dan Teknologi > S1 Teknik Sipil
Depositing User:	Kaprodi S1 Teknik Sipil UTY
Date Deposited:	10 Dec 2022 02:39
Last Modified:	10 Dec 2022 02:39
URI:	http://eprints.uty.ac.id/id/eprint/11843

Actions (login required)

View Item