PEMANFAATAN LIMBAH PLASTIK HDPE SEBAGAI BAHAN PEMBUATAN BATAKO DENGAN UJI KUAT TEKAN UTILIZATION OF HDPE PLASTIC WASTE AS A MATERIAL FOR MANUFACTURING BRICK WITH COMPRESSIVE STRENGTH TEST

Christensen, Rico and Kurniati, Dwi (2022) PEMANFAATAN LIMBAH PLASTIK HDPE SEBAGAI BAHAN PEMBUATAN BATAKO DENGAN UJI KUAT TEKAN UTILIZATION OF HDPE PLASTIC WASTE AS A MATERIAL FOR MANUFACTURING BRICK WITH COMPRESSIVE STRENGTH TEST. ["eprint_fieldopt_thesis_type_tugasakhir" not defined] thesis, University Technology Yogyakarta.

Text 5170811280_RICO CHRISTENSEN_ABSTRAK - Riko Christensen.pdf Download (25kB)

Abstract

Di Indonesia permasalahan plastik saat ini masih menjadi permasalahan terutama untuk sampah plastik. Plastik banyak digunakan dikarenakan plastik memiliki keungulan seperti praktis, kuat, ekonomis, ringan dan tahan korosi. Batako merupakan bahan bangunan yang berupa bata cetak alternatif penganti batu bata. Pada penelitian Tugas Akhir ini membahas mengenai pengujian mengunakan bahan limbah kantong plastik HDPE dan oli bekas dalam pembuatan batako plastik dengan komposisi 1: 2. Metode yang digunakan dalam analisis adalah metode eksprimental dengan memanfaatkan limbah plastic jenis HDPE dan limbah Oli yang digunakan untuk bahan pembuatan batako. Studi yang dilakukan yaitu untuk mengetahui pengujian kuat tekan. Peraturan yang digunakan dalam penelitian adalah SNI 03-0349-1989 bata beton untuk pasangan dinding. Berdasarkan analisis hasil pengujian kuat tekan, menunjukan nilai kuat tekan pada setiap benda uji diatas 39 Kg/cm² dimana murut SNI 03-0349-1989 batako tersebut termasuk kedalam mutu batako antara mutu batako III dan II, pada pengujian kuat tekan pada batako normal didapatkan nilai kuat tekan rata-rata sebesar 78,08 Kg/cm² sedangkan pada batako plastik jenis HDPE didapat kuat tekan rata-rata sebesar 58,07 Kg/cm². Kata kunci: Batako, Kuat Tekan, Plastik Jenis HDPE In Indonesia, the problem of plastic is still a problem, especially with plastic waste. Plastics are widely used because they have practical, substantial, economical, lightweight, and corrosion-resistant advantages. Brick is a building material in printed bricks as an alternative to bricks. This final project discusses testing using HDPE plastic bag waste materials and used oil to manufacture plastic bricks with a 1:2 composition. The method used in the analysis is an experimental method by utilizing HDPE type plastic waste and oil waste used for brick-making materials. The study was conducted to determine the compressive strength test. The regulations used in this study are SNI 03-0349-1989 concrete bricks for masonry walls. Based on the compressive strength test results, it shows the compressive strength value of each test object above 39 Kg/cm², where according to SNI 03-0349-1989, the brick is included in the quality of the brick between the quality of brick III and II. the average compressive strength of 78.08 Kg/cm² while the HDPE type plastic bricks obtained an average of 58.07 Kg/cm². Keywords: Brick, Compressive Strength, HDPE Type Plastic

Item Type:	Thesis (["eprint_fieldopt_thesis_type_tugasakhir" not defined])
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Fakultas Sains dan Teknologi > S1 Teknik Sipil
Depositing User:	Kaprodi S1 Teknik Sipil UTY
Date Deposited:	27 Dec 2022 02:37
Last Modified:	27 Dec 2022 02:37
URI:	http://eprints.uty.ac.id/id/eprint/11913

Actions (login required)

View Item